2715 Fiberglass insulation sleeving coated with polyvinyl Chloride resin
1 .Description: Electrical PVC fiberglass Insulation Sleeving is made from non-alkali fiberglass sleeving coated with polyvinyl chloride resin under the high temperature.
It is widely used as insulating and protection material for motor and electric appliance.
2.Specifications:
1).resistance temperature is 105°C
2).breakdown voltage:1.5kv 2.5kv 4.0 KV.
3).Diameter: 0.5-40 mm
4).Packing: 1meter or 50-100m/roll with carton or bag, can be according to customer's request
5).Color: red line, blue line and all kinds of color
| Model No. |
Product Name |
Components |
Temp. Class |
Features and Applications |
| Basic Material |
Impregnated
Varnish |
| 2715 |
Polyvinyl chloride coated fiberglass sleeving |
E-glass fiber braided sleeving |
Modified polyvinyl chloride resin |
A(105°C) |
- Excellent softness, elasticity,dielectric properties and chemical resistance
- As wiring insulation and mechanic protection for motor,electric instrument and radio equipment. |
| Item |
Unit |
Normal value |
| inner dia.& wall thickness(mm) |
mm |
inner dia(mm) |
wall thickness(mm) |
| |
|
standard |
tolerance |
min |
max |
| |
|
0.5;0.8 |
±0.10 |
0.20 |
0.50 |
| |
|
1.0;1.5;2.0;2.5;3.0 |
±0.15 |
0.20 |
0.75 |
| |
|
3.5;4.0;5.0;6.0;7.0;8.0 |
±0.25 |
0.30 |
0.75 |
| |
|
9;10;12;14;16;18;20 |
±0.50 |
0.40 |
0.90 |
| Bending after heating |
/ |
No cracking or detachment of coating shall be visible after bending around mandrels after 96h at 150ºC |
| Bending at low temperature |
|
No cracking or detachment of coating shall be visible after bending around mandrels while at -25ºC |
| Breakdown voltage |
kv |
|
Average |
Lowest |
| |
|
Room temp. |
4.0 |
2.5 |
| |
|
Elevated temp. |
1.2 |
0.8 |
| |
|
Damp heat |
1.2 |
0.8 |