Epoxy Glass Cloth Laminated Insulation Rod 3841

• Customization: Available
• Application: Electrical Maintenance, High Voltage Testing, Home Appliance Repair, Power Construction
• Color: Green, Blue, Black Color
• Model NO.: 3841
• Diameter: 6-50mm
• Material: Fiberglass
• Maximum Voltage: 20KV~100KV
• Thermal Rating: B 130
• Type: Insulation Rod
• Length: 1000mm-1100mm
• Nominal Diameter: 6mm-200mm
• Density: >1.70g/cm3
• Flexural Strength: >241.3MPa
• Compressive Strength: >241.3 MPa
• Breakdown Voltage Parallel to Layers,at: >15 Kv
• Chemistry: Inorganic Insulation
• Classification: Inorganic Insulation Material
• Certification: ISO9001
• Brand: Chr
• Transport Package: Wooden Pallet
• Specification: 6-200mm
• Trademark: CHR
• Origin: China
• HS Code: 8547909000
• Production Capacity: 200000kg/Week

Product Description

Product Description

3841 epoxy glass cloth laminate rod

Nominal diameter:6mm-200mm
Length:1000mm-1100mm
Epoxy glass cloth molded rod,  this grade can provide high mechanical strength at room temperature and has good dielectric and electric performance, low moisture absorption, as well as flame retardant.This grade is normally  used for electrical and electronic insulation when low moisture absorption and high mechanical strength are needed.

Product Parameters

PROPERTIES	UNIT	STANDARD VALUE
Flexural strength A: Under normal conditions	MPa	≥300
Compressive strength	MPa	≥175
Bonding strength	MPa	≥200
Breakdown voltage parallel to laminations (in transformer oil 90±2°C)	kV	≥40
Dielectric strength perpendicular to laminations  (withstand voltage) (in oil 90±2°C) 2.0mm in thickness	MV/m	≥9.0
Insulation resistance Impregnated in water, D-24/23	MΩ	≥1000
Density	g/cm^3	1.70-1.90
Water absorption D-24/23	mg/cm^2	≤1.5
Flammability	class	FV0

Item name	Epoxy phenolic glass cloth laminated rod
Item no.	3841
Feature	excellent insulation properties under dry and wet conditions. Used as insulating structural for electrical equipment. Temperature classification B.
Details
Properties	Unit	Index Value
diameter	mm		6-50
density	g/cm^3	≥1.70
flexural strength	Mpa	≥241.3
compressive strength	Mpa	≥241.3
breakdown voltage parallel to layers,at room temperature	KV	≥15 (in 90°C oil)